Ordered magnetic nanodot arrays with extremely high density provide unique properties to the growing field of nanotechnology. To overcome the size limitations of conventional lithography, a fine-tuned sputtering deposition process on mesoporous polymeric template fabricated by diblock copolymer self-assembly is herein proposed to fabricate uniform and densely spaced nanometer-scale magnetic dot arrays. This process was successfully exploited to pattern, over a large area, sputtered Ni80Fe20 and Co thin films with thicknesses of 10 and 13 nm, respectively. Carefully tuned sputter-etching at a suitable glancing angle was performed to selectively remove the magnetic material deposited on top of the polymeric template, producing nanodot arrays (dot diameter about 17 nm). A detailed study of magnetization reversal at room temperature as a function of sputter-etching time, together with morphology …